| 性能项目 | 试验条件[状态] | 测试方法 | 测试数据 | 数据单位 | |
| 物理性能 | 比重 | ASTM D792 | 1.76-1.78 | g/cm3 | |
| ISO 1183 | 1770 | kg/m3 | |||
| 熔体流动速率 | 450℃/5.0 kg | ASTM D1238 | 1.5-2.5 | g/10 min | |
| 熔体体积流动速率 | 230℃/5.0 kg | ISO 1133 | 1.1 | cm3/10min | |
| 吸水率 | 23℃, 24 hr | ASTM D570 | 0.01-0.03 | % | |
| 饱和 | ISO 62 | 0.03 | % | ||
| 平衡 | ISO 62 | 0.015 | % | ||
| 机械性能 | 硬度计硬度 | 支撐 D, 23℃ | ASTM D2240 | 77-82 | |
| 拉伸模量 | 23℃ | ASTM D638 | 1380-2310 | MPa | |
| ISO 527-2 | 2000 | MPa | |||
| 抗张强度 | 屈服, 23℃ | ASTM D638 | 44.8-55.2 | MPa | |
| 屈服 | ISO 527-2 | 50 | MPa | ||
| 断裂, 23℃ | ASTM D638 | 34.5-48.3 | MPa | ||
| 伸长率 | 屈服, 23℃ | ASTM D638 | 5-10 | % | |
| 屈服 | ISO 527-2 | 9 | % | ||
| 断裂, 23℃ | ASTM D638 | 20-100 | % | ||
| 断裂伸长率 | ISO 527-2 2 | > 50 | % | ||
| 拉伸蠕变模量 | 1 hr | 1050 | MPa | ||
| 1000 hr | 650 | MPa | |||
| 弯曲模量 | 23℃ | ASTM D790 | 1650-2310 | MPa | |
| 弯曲强度 | 5.0% 应变,23℃ | ASTM D790 | 58.6-75.8 | MPa | |
| 压缩强度 | 23℃ | ASTM D695 | 68.9-103 | MPa | |
| 摩擦系数 | 与钢 - 动态 | ASTM D1894 | 0.15 | ||
| 与钢 - 静态 | ASTM D1894 | 0.22 | |||
| 抗泰伯磨耗 | 1000 Cycles, 1000 g, CS-17 转轮 | 5-9 | mg | ||
| 简支梁缺口冲击强度 | -30℃ | ISO 179/1eA | 5 | kJ/m2; | |
| 23℃ | ISO 179/1eA | 22 | kJ/m2; | ||
| 简支梁冲击强度 | -30℃ | ISO 179/1eU | 201 | kJ/m2; | |
| 23℃ | ISO 179/1eU | 252 | kJ/m2; | ||
| 悬壁梁缺口冲击强度 | 23℃ | ASTM D256 | 96-210 | J/m | |
| 无缺口悬臂梁冲击 | 23℃ | ASTM D256 | 1100-4300 | J/m | |
| 热性能 | 热变形温度 | 1.8 MPa, 未退火 | ASTM D648 | 104-110 | ℃ |
| 1.8 MPa | ISO 75-2 | 104 | ℃ | ||
| 玻璃转化温度 | ISO 11357-2 | -40 | ℃ | ||
| DMA | -40.6 到 -38.3 | ℃ | |||
| 维卡软化点 | 50℃/h, B (50N) | ISO 306 | 138 | ℃ | |
| 熔融温度 | ASTM D3418 | 165-172 | ℃ | ||
| ISO 11357-3 | 169 | ℃ | |||
| 线形膨胀系数 - 流动 | ASTM D696 | 0.00012-0.00014 | cm/cm/℃ | ||
| ISO 11359-2 | 0.00015 | cm/cm/℃ | |||
| 比热 | DSC | 1170-1510 | J/kg/℃ | ||
| 导热系数 | ASTM C177 | 0.17-0.19 | W/m/K | ||
| 阻燃等级 | UL 94 | V-0 | |||
| 燃烧性能 正常厚度 1.6mm | 1.60 mm | ISO 1210 | V-0 | ||
| 一定厚度与小时下的阻燃等级 | 0.800 mm | ISO 1210 | V-0 | ||
| 电气性能 | 表面电阻率 | IEC 60093 | 4.0E+13 | ohm | |
| 体积电阻率 | 20℃ | ASTM D257 | 2.0E+14 | ohm·cm | |
| IEC 60093 | 2.3E+10 | ohm·cm | |||
| 介电强度 | 23℃ | ASTM D149 | 63 | kV/mm | |
| IEC 60243-1 | 27 | kV/mm | |||
| 介电常数 | 23℃ | ASTM D150 | 4.5-9.5 | ||
| 100 Hz | IEC 60250 | 10.5 | |||
| 1 MHz | IEC 60250 | 7 | |||
| 耗散因数 | 23℃, 100 Hz | ASTM D150 | 0.1-0.25 | ||
| 100 Hz | IEC 60250 | 0.027 | |||
| 1 MHz | IEC 60250 | 0.24 | |||
| 漏电起痕指数 | IEC 60112 | 600 | |||
| 光学性能 | 折射率 | ASTM D542 | 1.42 | ||
| 其它 | 极限氧指数 | ASTM D2863 | 60 | % | |
| ASTM D2863 | 83 | % | |||